TPE 85A
A soft 85A TPE for grips, sleeves and skin-contact parts.
Price, availability and delivery are confirmed by enquiry. Your selected SKU and spool option travel with your request.
PRINTING PARAMETERS
Starting points for your slicer.
From the company parameter sheet. Confirm the profile against your own printer, nozzle and build surface before a production run.
A soft TPE 85A filament range for flexible grips, sleeves and tactile parts. The Sungallon presentation lists 85 Shore A, 6.0 MPa tensile strength and 470% elongation as typical selection values; confirm the current SKU documentation and printer profile before production.
The parameter sheet repeats the column header for this grade, so its column could not be matched to the grade with certainty. Treat these values as indicative until R&D confirms them.
| Nozzle diameter | 0.4mm |
|---|---|
| Flow ratio | 0.96-1.10 (rec. 0.96) |
| Bed temperature | 60-70°C (rec. 65) |
| Nozzle temperature | 225-245°C (rec. 230) |
| Cooling fan | 50-80% |
| Retraction (direct drive) | 0.4-1.2mm |
| Retraction (Bowden) | Not recommended |
| Max volumetric speed | 2.8mm³/s |
| Recommended print speed | ≤60mm/s |
| Density (g/cm³) | 0.9-1.1 |
|---|---|
| Melt flow index (200 °C / 2.16 kg) | 8.6-10 |
| Heat deflection temperature (°C) | — |
| Vicat softening temperature (°C) | — |
| Tensile strength (MPa) | 4-6.7 |
| Tensile strength, X axis (MPa) | — |
| Tensile strength, Y axis (MPa) | — |
| Tensile strength, Z axis (MPa) | — |
| Elongation at break (%) | <500 |
| Flexural strength (MPa) | — |
| Flexural modulus (MPa) | — |
| Impact strength (kJ/m²) | — |